| Categories | Titanium Alloy |
|---|---|
| Brand Name: | JIMA Aluminum |
| Model Number: | 8011,3003，5005,5052 |
| Certification: | IRIS,ISO9001，ISO 14001. |
| Place of Origin: | CHINA |
| MOQ: | Negotiations |
| Price: | Negotiations |
| Payment Terms: | T/T, L/C |
| Supply Ability: | 2000 MT per month |
| Delivery Time: | 20~25days |
| Packaging Details: | wooden pallet |
| Name: | TC4 (Ti-6Al-4V) Titanium Alloy Rods and Bars |
| Alloy: | TC4 (Ti-6Al-4V) |
| Execution Standards: | GB/T 2965 GJB 2218A GJB 1538A AMS 4928, ASTM B348, AMS-T-9047 |
| Application: | Materials used in aerospace, automotive and new energy, industrial molds and dies, and semiconductor fields |
Unique Advantages | Main Applications | Execution Standards |
1.Excellent corrosion resistance | 1.Medical components | GB/T 2965 |
2.Excellent fatigue strength | 2.Chemical components | GJB 2218A |
3.Good machinability | 3.Marine components | GJB 1538A |
4.Good strength-to-weight ratio | 4.Racing components | AMS 4928, ASTM B348, AMS-T-9047 |
Element | Ti | Al | V | Fe | C | N | H | O | Other Single | Other Total |
Min | Balance | 5.5 | 3.5 | |||||||
Max | Balance | 6.75 | 4.5 | 0.3 | 0.08 | 0.05 | 0.015 | 0.2 | 0.1 | 0.4 |
Room Temperature Tensile Properties | High Temperature Mechanical Properties | ||
Minimum | Minimum | ||
Tensile Strength (Rm) / MPa | 895 | Tensile Strength (Rm) / MPa | 600 |
Yield Strength (Rp0.2) / MPa | 827 | Test Stress (σ) / MPa | 560 |
Elongation after Fracture (A) / % | 10 | Test Time (t) / h | 100 |
Reduction of Area (Z) / % | 25 | Test Temperature / ℃ | 400 |
6,Mechanical/Mechanical Properties of Titanium and Titanium Alloy
Plates Alloy | Condition | Thickness Range/mm | Tensile Strength (Rm)/MPa | Yield Strength (Rp0.2)/MPa | Elongation after Fracture /% ≥ | Bending Radius |
TA2 | M | 0.3 - 1.0 | 440 - 620 | ≥320 | ≥35 | ≥100°, 3t |
> 1.0 - 2.0 | 440 - 620 | ≥320 | ≥30 | ≥100°, 3t | ||
> 2 - 5.0 | 440 - 620 | ≥320 | ≥25 | ≥90°, 3t | ||
> 5 - 10.0 | 440 - 620 | ≥320 | ≥25 | - | ||
> 10.0 - 30 | 440 - 620 | ≥320 | ≥18 | - | ||
TC4 | M | 0.5 - 1.8 | 925 - 1150 | ≥870 | ≥12 | ≥105°, 9t |
> 1.8 - 4.0 | 925 - 1150 | ≥870 | ≥12 | ≥105°, 10t | ||
> 4.0 - 5.0 | 925 - 1150 | ≥870 | ≥10 | ≥105°, 10t | ||
> 5.0 - 10.0 | 925 - 1150 | ≥825 | ≥10 | - | ||
> 10.0 - 100 | 925 - 1150 | ≥825 | ≥9 | - |
Alloy | Condition | Thickness Range/mm | Tensile Strength (Rm)/MPa | Test Temperature/℃ | Test Stress(σ)/MPa | Test Time(t)/h |
TC4 | M | 0.5 - 30.0mm | ≥590 | 400 | 540 | ≥100 |
≥540 | 500 | 195 |
|
TA1 TA2 TC4 GR1 High Strength Aerospace Titanium Forged Components
Forged Titanium Rings For Aerospace TA1 TA9 GR1 For Aircraft & Aerospace Parts
TC4 (Ti-6Al-4V) Titanium Sheet For Aerospace High Performance Materials For Aircraft
TA2 Industrial Pure Titanium Titanium Rod For Automotive And Energy Production
TA2 Industrial Pure Titanium Plate GB/T 2965 Standards