| Categories | Alumina Ceramic Grinding Balls |
|---|---|
| Alumina Content: | 92%,95%,99% |
| Hardness: | 9 |
| Size: | Can be customized design |
| Application: | As a grinding and polishing material,for the electronics industry |
| Place of Origin: | Zibo, Shandong |
| Brand Name: | HUAO |
| Certification: | ISO9001 ISO14001 ISO45001 |
| Model Number: | OEM |
zirconia ceramic ball
Introduction
The wear-resistant medium of zirconium silicate beads is made of high-purity ultra-fine zirconium silicate powder, which has a uniform microcrystalline structure and no hollow inside. Compared with the electrofusion method and other zirconium silicate beads, the strength of zirconium silicate beads is higher and the cost performance is better. The microstructure of the beads is composed of dense zirconium silicate particles, which rejects the gap and cavity, avoids the separation of crystalline phase and glass phase, and has greater density and hardness than similar beads. Medium density and hardness suitable for medium and low viscosity slurry dispersion and grinding, can match most of the sand mill, for the universal grinding medium
Properties
Wear-resistant, not broken beads, very suitable for paint, coating, paper mill.
Dense crystalline phase structure high strength, wear;
Special ingredient high density high grinding efficiency;
High sphericity good fluidity large flow of material;
Solid bead not easy to break; Convenient color change;
Smooth spherical surface easy to clean; Small wear to the equipment;
Uniform particle size internal friction of beads; The particle size distribution of the milled product was uniform.
Size
∅0.2-0.4mm | ∅0.4-0.6mm | ∅0.6-0.8mm | ∅0.8-1.0mm | ∅1.0-1.2mm |
∅1.2-1.4mm | ∅1.4-1.6mm | ∅1.5-2.0mm | ∅2.0-2.5mm | ∅2.5-3.0mm |
∅3.0-3.5mm | ∅4mm | ∅5mm | ∅8mm | ∅10mm |
Technical data
ZTA280 | ZTA320 | ZTA370 | ZTA380 | ZTA450 | ZTA470 | |
AL2O3(%) | ≥57 | ≥70 | ≥87 | ≥66 | ≥5 | ≥3 |
ZrO2(%) | ≥5 | ≥5 | ≥5 | ≥18 | ≥62 | ≥70 |
SiO2(%) | ≤30 | ≤20 | ≤5 | ≤12 | ≤30 | ≤24 |
Bulk density(g/cm³) | ≥2.80 | ≥3.15 | ≥3.70 | ≥3.78 | ≥4.48 | ≥4.60 |
HV Hardness(Gpa) | ≥7 | ≥8 | ≥12.5 | ≥11 | ≥10 | ≥10 |
Crushing Strength(N) | ≥25 (∅1.5-2) | ≥800 (∅13.5) | ≥1000 (∅3) | ≥12000 (∅8) | ≥1200 (∅3) | ≥1300 (∅3) |
Water absorption | ＜0.01 | ＜0.01 | ＜0.01 | ＜0.01 | ＜0.01 | ＜0.01 |
Wear loss rate(g/kg.h) | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
Sphericity | ≥95% | ≥95% | ≥95% | ≥95% | ≥95% | ≥95% |
|
Wear Resistant White Alumina Ceramic Balls Size 13-90mm
92% Alumina Ceramic Grinding Media Al2o3 Ball For Cement Mill
92% 95% Al2O3 Alumina Ceramic Ball For Cement Grinding
ZTA Ceramic Grinding Beads Zirconia Toughened Alumina 92%
Wear Resistant High Alumina Ceramic Milling Balls 60% 92% 95% 99%
Wear Resistant Alumina Ceramic Grinding Balls 90% 92% 95% 99% Al2O3
92% Ceramic Alumina Balls Beads With High Temperature Resistance
13-90mm Alumina Ceramic Grinding Balls For Vibration Mill
9 Mohs Hardness High Alumina Ceramic Balls 3.6-3.8 G/Cm3
0.2-3.5mm Alumina Ceramic Grinding Balls Zirconia Grinding Beads